The article shows our R&D findings on alternative materials for repair systems of wind turbine blades. The repair unit from structrepair GmbH causes a significant reduction in repair time due to short time curing of the prepreg, while extending repair SEASON during unfavorable weather conditions.

Preview in English:
Epoxy resin prepregs were stored for 9–90 days at room temp. and then studied for reactivity as well as thermal and mech. properties. Reactivity changes were obsd. by DSC anal. and viscosity changes during dynamic tests. Crosslinked laminates were also obtained after the same storage times. Thermal and mech. properties were detd. by DMA and static tensile tests, resp. Adhesion was detd. by in-house field test by using 6 prepreg layers. The reactivity decreased during the storage, esp. between 13. and 23. days but without any significant effect on thermal resistance and mech. strength.

Preview in Polish:
Przedstawiono wyniki badań wpływu procesu starzenia (przechowywania) na reaktywność oraz właściwości termiczne i mechaniczne prepregów na bazie żywic epoksydowych. Stwierdzono, że w czasie przechowywania w temperaturze pokojowej reaktywność maleje, zwłaszcza pomiędzy 13. a 23. dniem składowania, bez wpływu na wytrzymałość mechaniczną i termiczną uzyskanych laminatów. Ponadto nie zaobserwowano obniżenia adhezji do wybranego podłoża. Opracowane materiały stanowią alternatywę dla obecnie stosowanych materiałów naprawczych do łopat elektrowni wiatrowych.

Download the article in Polish here: Prepregs based on epoxy resin as a repair material for wind turbine blades (953.9 KB)

Read article on LinkedIn:

Interested in the subject? Contact our R&D Department to find out more.